Sinkral® PD D 232/M4
Units 
Versalis S.p.A. - Acrylonitrile Butadiene Styrene
ActionLegend (Open)
Request for Quote E-mail a Datasheet Print this Page  

General Information
Product Description
Special very low gloss extrusion / co-extrusion grade, with good flow.

Designation: Thermoplastic ISO 2580-ABS 1,EGN,105-08-09-15

Sinkral PD D 232/M4 is widely used in the extrusion / co-extrusion of foils, when a very high matt appearance is required, as well as in the extrusion of profiles.

This grade is available in natural color only
General  
Material Status 
  • Commercial: Active
Availability 
  • Africa & Middle East
  • Asia Pacific
  • Europe
  • Latin America
  • North America
Features 
  • Good Flow
  • Low Gloss
 
Uses 
  • Profiles
Appearance 
  • Matte Finish
  • Natural Color
 
Forms 
  • Pellets
Processing Method 
  • Coextrusion
  • Extrusion
  • Profile Extrusion
ASTM & ISO Properties 1
Physical
Nominal Value
Unit
Test Method
Density
1.04
g/cm³
ISO 1183
Melt Mass-Flow Rate (MFR) (220°C/10.0 kg)
8.0
g/10 min
ISO 1133
Molding Shrinkage
0.40 to 0.60
%
Internal Method
Water Absorption (23°C, 24 hr)
0.30
%
ASTM D570
Mechanical
Nominal Value
Unit
Test Method
Tensile Strength 2
27.0
MPa
ASTM D638
Tensile Elongation 2 (Break)
100
%
ASTM D638
Flexural Modulus 3
1550
MPa
ASTM D790
Flexural Strength 3
40.0
MPa
ASTM D790
Impact
Nominal Value
Unit
Test Method
Charpy Notched Impact Strength (23°C)
9.0
kJ/m²
DIN 53453
Charpy Unnotched Impact Strength
    DIN 53453
-40°C
No Break
 
 
23°C
No Break
 
 
Notched Izod Impact
    ISO 180/4A
-40°C, 3.20 mm
75
J/m
 
-20°C, 3.20 mm
80
J/m
 
0°C, 3.20 mm
90
J/m
 
23°C, 3.20 mm
110
J/m
 
Notched Izod Impact Strength 4
    ISO 180/1A
-40°C
7.0
kJ/m²
 
23°C
9.5
kJ/m²
 
Hardness
Nominal Value
Unit
Test Method
Rockwell Hardness (R-Scale)
97
 
ISO 2039-2
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed)
101
°C
ASTM D648
Vicat Softening Temperature
     
--
106
°C
ISO 306/A120
--
101
°C
ISO 306/B120
CLTE - Flow
0.000090
cm/cm/°C
ASTM D696
Thermal Conductivity
0.17
W/m/K
ASTM C177
Electrical
Nominal Value
Unit
Test Method
Surface Resistivity
1.0E+14
ohm
IEC 60093
Volume Resistivity
1.0E+15
ohm·cm
IEC 60093
Electric Strength
30
kV/mm
IEC 60243-1
Dielectric Constant (1 kHz)
3.10
 
IEC 60250
Dissipation Factor (1 kHz)
0.015
 
IEC 60250
Flammability
Nominal Value
Unit
Test Method
Flame Rating (1.50 mm)
HB
 
UL 94
Glow Wire Ignition Temperature (3.00 mm)
650
°C
IEC 60695-2-13
Additional Information
Nominal Value
Unit
Test Method
Designation
Thermoplastic ISO 2580-ABS 1,EGN,105-08-09-15
 
 
Processing Information
Extrusion
Nominal Value
Unit
 
Drying Temperature
80.0
°C
 
Drying Time
2.0 to 4.0
hr
 
Melt Temperature
180 to 220
°C
 
Notes
1Typical properties: these are not to be construed as specifications.
250 mm/min
32.0 mm/min
44 mm
 
UL IDES

UL and the UL logo are trademarks of UL LLC © . All Rights Reserved.

Nominal ValueThe information presented on this datasheet was acquired by UL Prospector from the producer of the material. UL Prospector makes substantial efforts to assure the accuracy of this data. However, UL Prospector assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.