Density / Specific Gravity
|
1.42
|
g/cm³
|
ASTM D792 |
|
Density
|
1.42
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
|
12
|
g/10 min
|
ISO 1133 |
|
Molding Shrinkage -
Flow
|
1.8 to 2.2
|
%
|
Internal Method |
|
Water Absorption (24 hr, 23°C, 50% RH)
|
0.20
|
%
|
ASTM D570 |
|
Tensile Modulus
|
2900
|
MPa
|
ISO 527-1 |
|
Tensile Strength
|
67.0
|
MPa
|
ASTM D638 |
|
Tensile Stress (Yield)
|
68.0
|
MPa
|
ISO 527-2 |
|
Tensile Elongation (Break)
|
45
|
%
|
ASTM D638 |
|
Nominal Tensile Strain at Break
|
45
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
2800
|
MPa
|
ASTM D790 |
|
Flexural Modulus
|
2700
|
MPa
|
ISO 178 |
|
Flexural Strength
|
95.0
|
MPa
|
ASTM D790 |
|
Taber Abrasion Resistance
|
13.0
|
mg
|
ASTM D1044 |
|
Charpy Notched Impact Strength
|
10
|
kJ/m²
|
ISO 179 |
|
Notched Izod Impact
|
85
|
J/m
|
ASTM D256 |
|
Rockwell Hardness
|
|
|
ASTM D785 |
|
M-Scale
|
92
|
|
|
|
R-Scale
|
120
|
|
|
|
Deflection Temperature Under Load (0.45 MPa, Unannealed)
|
172
|
°C
|
ASTM D648 |
|
Deflection Temperature Under Load (0.45 MPa, Unannealed)
|
155
|
°C
|
ISO 75-2/B |
|
Deflection Temperature Under Load (1.8 MPa, Unannealed)
|
125
|
°C
|
ASTM D648 |
|
Deflection Temperature Under Load (1.8 MPa, Unannealed)
|
90.0
|
°C
|
ISO 75-2/A |
|
CLTE -
Flow
|
1.0E-4
|
cm/cm/°C
|
ASTM D696 |
|
CLTE -
Flow
|
1.0E-4
|
cm/cm/°C
|
ISO 11359-2 |
|
Dielectric Strength
|
18
|
kV/mm
|
ASTM D149 |
|
Arc Resistance
|
250
|
sec
|
ASTM D495 |
|
Flame Rating
|
|
|
UL 94 |
|
0.75 mm
|
HB
|
|
|
|
1.5 mm
|
HB
|
|
|