Density / Specific Gravity
|
1.23
|
--
|
g/cm³
|
ASTM D792 |
|
Density
|
1.23
|
--
|
g/cm³
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (275°C/5.0 kg)
|
75
|
--
|
cm³/10min
|
ISO 1133 |
|
Molding Shrinkage -
Flow
(3.18 mm)
|
0.50
|
--
|
%
|
|
|
Water Absorption (Saturation)
|
7.7
|
--
|
%
|
ASTM D570 |
|
Water Absorption (Saturation, 23°C)
|
7.7
|
--
|
%
|
ISO 62 |
|
Water Absorption (Equilibrium, 50% RH)
|
2.3
|
--
|
%
|
ASTM D570 |
|
Water Absorption (Equilibrium, 23°C, 50% RH)
|
2.3
|
--
|
%
|
ISO 62 |
|
Tensile Modulus (23°C)
|
5800
|
3500
|
MPa
|
ISO 527-1 |
|
Tensile Strength (Break, 23°C)
|
103
|
--
|
MPa
|
ASTM D638 |
|
Tensile Stress (Break, 23°C)
|
130
|
70.0
|
MPa
|
ISO 527-2 |
|
Tensile Elongation (Break, 23°C)
|
3.5
|
--
|
%
|
ASTM D638 |
|
Tensile Strain (Break, 23°C)
|
3.5
|
15
|
%
|
ISO 527-2 |
|
Flexural Modulus (23°C)
|
5170
|
--
|
MPa
|
ASTM D790 |
|
Flexural Modulus (23°C)
|
5200
|
2500
|
MPa
|
ISO 178 |
|
Charpy Notched Impact Strength
|
|
|
|
ISO 179 |
|
-30°C
|
7.0
|
--
|
kJ/m²
|
|
|
23°C
|
8.0
|
20
|
kJ/m²
|
|
|
Charpy Unnotched Impact Strength
|
|
|
|
ISO 179 |
|
-30°C
|
45
|
--
|
kJ/m²
|
|
|
23°C
|
50
|
110
|
kJ/m²
|
|
|
Notched Izod Impact
|
|
|
|
ASTM D256 |
|
-40°C
|
48
|
--
|
J/m
|
|
|
23°C
|
59
|
--
|
J/m
|
|
|
Notched Izod Impact Strength (23°C)
|
6.0
|
--
|
kJ/m²
|
ISO 180 |
|
Deflection Temperature Under Load (0.45 MPa, Unannealed)
|
215
|
--
|
°C
|
ASTM D648 |
|
Deflection Temperature Under Load (0.45 MPa, Unannealed)
|
215
|
--
|
°C
|
ISO 75-2/B |
|
Deflection Temperature Under Load (1.8 MPa, Unannealed)
|
190
|
--
|
°C
|
ASTM D648 |
|
Deflection Temperature Under Load (1.8 MPa, Unannealed)
|
190
|
--
|
°C
|
ISO 75-2/A |
|
Peak Melting Temperature
|
220
|
--
|
°C
|
ASTM D3418 |
|
Melting Temperature (DSC)
|
220
|
--
|
°C
|
ISO 3146 |
|
CLTE -
Flow
|
2.0E-5
|
--
|
cm/cm/°C
|
ASTM E831 |
|
CLTE -
Flow
|
3.3E-5
|
--
|
cm/cm/°C
|
|
|
CLTE -
Transverse
|
7.5E-5
|
--
|
cm/cm/°C
|
|
|
RTI Elec
|
|
|
|
UL 746B |
|
0.8 mm
|
120
|
--
|
°C
|
|
|
1.5 mm
|
120
|
--
|
°C
|
|
|
3.0 mm
|
120
|
--
|
°C
|
|
|
RTI Imp
|
|
|
|
UL 746B |
|
1.5 mm
|
95.0
|
--
|
°C
|
|
|
3.0 mm
|
95.0
|
--
|
°C
|
|
|
RTI Str
|
|
|
|
UL 746B |
|
1.5 mm
|
130
|
--
|
°C
|
|
|
3.0 mm
|
130
|
--
|
°C
|
|
|
Volume Resistivity (1.50 mm)
|
1.0E+15
|
1.0E+12
|
ohms·cm
|
ASTM D257 |
|
Volume Resistivity
|
1.0E+15
|
1.0E+12
|
ohms·cm
|
IEC 60093 |
|
Dielectric Constant (1 MHz)
|
3.80
|
7.00
|
|
IEC 60250 |
|
Dissipation Factor
|
|
|
|
IEC 60250 |
|
100 Hz
|
0.025
|
0.24
|
|
|
|
1 MHz
|
0.025
|
0.24
|
|
|
|
Flame Rating
|
|
|
|
UL 94 |
|
1.5 mm
|
HB
|
--
|
|
|
|
3.0 mm
|
HB
|
--
|
|
|