Lupolen 2420F PLUS
Units 
LyondellBasell Industries - Low Density Polyethylene
ActionLegend (Open)
E-mail a Datasheet Print this Page  

General Information
Product Description
Lupolen 2420 F PLUS is a non-additivated, low density polyethylene. This grade is characterized by a very low gel level. Typical customer applications are surface protection films or other higher value film applications where a very low gel content is required . It is delivered in pellet form.
This product is not intended for use in medical and pharmaceutical applications.
General  
Material Status 
  • Commercial: Active
Availability 
  • Africa & Middle East
  • Asia Pacific
  • Europe
Features 
  • General Purpose
  • Good Heat Seal
  • Good Melt Strength
  • Good Optical Properties
  • Good Processability
  • Low Gel
Uses 
  • Bags
  • Film
  • Flexible Packaging
  • Food Packaging
  • Hygiene
  • Liners
  • Pouches - Flexible Packaging
  • Protective Coatings
  • Shrink Wrap
Processing Method 
  • Blown Film
Properties 1
Physical
Nominal Value
Unit
Test Method
Density
0.923
g/cm³
 ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
0.75
g/10 min
 ISO 1133
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
260
MPa
 ISO 527-1
Tensile Stress (Yield)
11.0
MPa
 ISO 527-2
Coefficient of Friction
> 0.80
 
 ISO 8295
Films
Nominal Value
Unit
Test Method
Film Thickness - Tested 2
50
µm
  
Tensile Strength
     ISO 527-3
MD
26.0
MPa
  
TD
24.0
MPa
  
Tensile Elongation
     ISO 527-3
MD : Break
300
%
  
TD : Break
600
%
  
Dart Drop Impact 3
150
g
 ASTM D1709
Thermal
Nominal Value
Unit
Test Method
Vicat Softening Temperature
96.0
°C
 ISO 306/A50
Melting Temperature
111
°C
 ISO 11357-3
Optical
Nominal Value
Unit
Test Method
Gloss
     ASTM D2457
20°
> 40
 
  
60°
> 90
 
  
Haze (50.0 µm)
< 8.00
%
 ASTM D1003
Additional Information
Nominal Value
Unit
Test Method
Failure Energy
55.0
J/cm
 DIN 53373
Processing Information
Extrusion
Nominal Value
Unit
 
Melt Temperature
170 to 220
°C
  
Notes
1Typical properties: these are not to be construed as specifications.
2Film properties tested using 50 µm thickness blown film extruded at a melt temperature of 180°C and a blow-up ratio of 2.5:1
3F50
 
Customer is responsible for determining whether products and the information in this document are appropriate for Customer’s use and for ensuring that Customer’s workplace and disposal practices are in compliance with applicable laws and other governmental enactments. Seller assumes no obligation or liability for the information in this document. NO WARRANTIES ARE GIVEN; ALL IMPLIED WARRANTIES OF MERCHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE ARE EXPRESSLY EXCLUDED.