Density
|
1.37
|
g/cm³
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (360°C/10.0 kg)
|
35
|
cm³/10min
|
ISO 1133 |
|
Molding Shrinkage
|
|
|
ISO 294-4 |
|
Across Flow
|
0.90
|
%
|
|
|
Flow
|
0.85
|
%
|
|
|
Water Absorption (Saturation, 23°C)
|
2.2
|
%
|
ISO 62 |
|
Water Absorption (Equilibrium, 23°C, 50% RH)
|
0.80
|
%
|
ISO 62 |
|
Tensile Modulus (23°C)
|
2650
|
MPa
|
ISO 527-1 |
|
Tensile Stress (Yield, 23°C)
|
85.0
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Yield, 23°C)
|
6.9
|
%
|
ISO 527-2 |
|
Charpy Notched Impact Strength
|
|
|
ISO 179 |
|
-30°C
|
8.0
|
kJ/m²
|
|
|
23°C
|
8.0
|
kJ/m²
|
|
|
Charpy Unnotched Impact Strength
|
|
|
ISO 179 |
|
-30°C
|
No Break
|
|
|
|
23°C
|
No Break
|
|
|
|
Notched Izod Impact Strength
|
|
|
ISO 180 |
|
-30°C
|
8.0
|
kJ/m²
|
|
|
23°C
|
8.0
|
kJ/m²
|
|
|
Ball Indentation Hardness
|
154
|
MPa
|
ISO 2039-1 |
|
Deflection Temperature Under Load (1.8 MPa, Unannealed)
|
207
|
°C
|
ISO 75-2/A |
|
CLTE -
Flow
|
5.2E-5
|
cm/cm/°C
|
|
|
RTI Elec
|
|
|
UL 746B |
|
1.6 mm
|
180
|
°C
|
|
|
3.0 mm
|
180
|
°C
|
|
|
RTI Imp
|
|
|
UL 746B |
|
1.6 mm
|
180
|
°C
|
|
|
3.0 mm
|
180
|
°C
|
|
|
RTI Str
|
|
|
UL 746B |
|
1.6 mm
|
190
|
°C
|
|
|
3.0 mm
|
190
|
°C
|
|
|
Surface Resistivity
|
> 1.0E+15
|
ohms
|
IEC 60093 |
|
Volume Resistivity
|
> 1.0E+15
|
ohms·cm
|
IEC 60093 |
|
Electric Strength
|
34
|
kV/mm
|
IEC 60243-1 |
|
Dielectric Constant
|
|
|
IEC 60250 |
|
100 Hz
|
3.90
|
|
|
|
1 MHz
|
3.80
|
|
|
|
Dissipation Factor
|
|
|
IEC 60250 |
|
100 Hz
|
1.7E-3
|
|
|
|
1 MHz
|
0.014
|
|
|
|
Comparative Tracking Index
|
125
|
V
|
IEC 60112 |
|
Flame Rating
|
|
|
UL 94 |
|
1.6 mm
|
V-0
|
|
|
|
3.0 mm
|
V-0
|
|
|